Corundum Bricks

 

Brand

Properties
WA99
WA98
WA97
WA95
WA93
WA90
Max service temperature (¡ãC)
1850
1850
1800
1750
1700
1650
Al2O3% ¡Ý
99
98
97
95
93
90
Fe2O3 ¡Ü
0.15
0.2
0.3
0.4
0.5
0.8
Bulk density ¡Ý g/cm3
3.15
3.15
3.1
3.0
2.95
2.90
Apparent Porosity ¡Ü%
20
20
20
20
20
20
Cold Crushing Strength MPa ¡Ý
90
90
80
80
80
80
0.2MPa Refractoriness under load ¡ãC¡Ý
1800
1800
1750
1700
1700
1600
Permanent linear change %
¡À0.1
(1700¡ãC¡Á2h)
¡À0.15
(1700¡ãC¡Á2h)
¡À0.2
(1700¡ãC¡Á2h)
¡À0.2
(1650¡ãC¡Á2h)
¡À0.3
(1650¡ãC¡Á2h)
¡À0.3
(1600¡ãC¡Á2h)

Raw material

Corundum Bricks


Mullite Bricks

Item

Properties
Mullite Bricks
Corundum Mullite
Corumdum-Mullite Bricks for Kiln furniture
Cordierite-mullite Bricks for kiln Furniture
SAS-70
FAS-70
Al2O3% ¡Ý
70
70
85
85
45
SiO2 %¡Ü
24
25
12.5
40-45
Fe2O3 %¡Ü
1.0
0.5
0.5
1.0
1.4
R2O% ¡Ü
1.5
0.5
Bulk Density ¡Ý g/cm3
2.55
2.58
2.85
1.8-2.2
Apparent Porosity ¡Ü %
17
16
15
30
Cold Crushing Strength Mpa ¡Ý
45
80
85
110
40
0.2MPa Refractoriness under load ¡ãC¡Ý
1650
700
1700
1700
1380
Permanent linear change %
¡À0.1
(1600¡ãC¡Á2h)
¡À0.1
(1650¡ãC¡Á2h)
¡À0.2
(1650¡ãC¡Á2h)
Cold Bending Strength Mpa ¡Ý
15
20
15
8
High temperature Bending Strength Mpa ¡Ý
8
12
11
12
8
Thermal shock Resistance (water cycle) (1100¡ãC)¡Ý
25
30
40
25
40
Thermal expansion coeffient (1000¡ãC)
3.3

Raw material

Corundum Mullite Bricks